Molecular Sieve type 5A is an alkali alumino silicate; it is the calcium form of the Type A crystal structure. Type 5A has an effective pore opening of 5 angstroms (0.5 nm). It will adsorb molecules with a kinetic diameter of less than 5 Angstrom and exclude those larger.
Bu PSA vodorod tozalash va kislorod kontsentratorlari yilda, normal va ISO-parafinler (C4to C6 turlari) bo'linishi uchun foydalanish mumkin MTB adsorber ilovalar uchun, ayniqsa, javob beradi.
Texnik-parametr
|
model |
5A |
|||
|
rang |
Light kulrang |
|||
|
Nominal gözenek diametri |
5 angstromdur |
|||
|
Shape |
soha |
shar |
||
|
Diametri (mm) |
1.7-2.5 |
3.0-5.0 |
1,6 |
3,2 |
|
sinfga hajmi nisbati qadar (%) |
≥98 |
≥98 |
≥96 |
≥96 |
|
Quyma zichligi (g / ml) |
≥0.72 |
≥0.70 |
≥0.66 |
≥0.66 |
|
Wear nisbati (%) |
≤0.20 |
≤0.20 |
≤0.20 |
≤0.20 |
|
Xafa qilma kuch (N) |
≥45 / parcha |
≥100 / parcha |
≥40 / parcha |
≥75 / parcha |
|
Statik H 2O yutish (%) |
≥22 |
≥22 |
≥22 |
≥22 |
|
Suv tarkibi (%) |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
|
Odatda Kimyoviy Formula |
0.7CaO. 0.3Na 2O. Al 2O 3. 2SiO 2. 4.5H 2O |
|||
|
Odatda Application |
a) divalent kaltsiy ionlarining kuchli ion kuchlari suv, CO olib tashlash uchun ajoyib adsorbent qiladi 2, H 2mini cos shakllanishini bedarak esa, nordon, tabiiy gaz akımlarından S. Light Merkaptanlar ham tutiladi. |
|||
|
Paket: |
Karton quti; Karton drum; Temir drum |
|||
|
MOQ: |
1 metrik tonna |
|||
|
To'lov shartlari: |
T / T; L / C; PayPal; G'arbiy Ittifoqi |
|||
|
kafolat: |
a) Milliy Standard GB_13550-1992 qasamki |
|||
|
b) muammolar bo'yicha taklif umrbod maslahat sodir |
||||
|
Idish |
20GP |
40GP |
Misol buyurtma |
|
|
miqdor |
12MT |
24MT |
<5kg |
|
|
Yetkazish vaqti |
3 kun |
5 kun |
mavjud fond |
|
Size regeneratsiyasi
molekulyar oldin turi 5A issiqlik tebranish jarayonlarining holda ham isitish, qayta tuzilishi mumkin; yoki bosim tebranish jarayonlarining holda bosim pasaytirish orqali.
A 5A molekulyar oldin namlik olib tashlash uchun, 250-300 ° C harorat talab qilinadi. A to'g'ri rejenere molekulyar oldin -100 ° C dan past namlik shudring ball beringlar, yoki Merca ptan yoki CO2 sathi 2 ppm quyida mumkin.
Bosim tebranish jarayoni outlet kontsentratsiyasi gaz Ayni bog'liq va jarayonning sharoitiga bo'ladi.
5A - Zeolitleri, 1-2 mm (10 × 18 oro), 2-3 mm (8 × 12 oro), 2.5-5 mm (4 × 8 mash tortish) va chang, deb ibodati mavjud, va shar har 1,6 mm'ye bilan 3.2mm.
Diqqat
yugurib oldin organik nam va oldindan adsorbsiyonu oldini olish uchun, yoki qayta faollashtirib uchun kerak.